META-THIN Pour Supplies by Metallurgical Supplies

META-Thin Pour 130mlMETA-Thin Pour 130ml
Model: REP-MTP-KITBrand: Metallography World Corporation
 META-Thin Pour 130ml Thin Pour Physical Properties   Quick Casting – Zero Shrinkage META-THIN Pour Physical Properties & Applications Mix Time 30 - 45 Seconds Working Time 2 Minutes Set..
META-Thin Pour 380ml kitMETA-Thin Pour 380ml kit
Model: REP-MTP-01Brand: Metallography World Corporation
 META-Thin Pour 380ml kit Thin Pour Physical Properties   Quick Casting – Zero Shrinkage META-THIN Pour Physical Properties & Applications Mix Time 30 - 45 Seconds Working Time 2 Minutes ..
META-Thin Pour Case of 10 380ml kitsMETA-Thin Pour Case of 10 380ml kits
Model: REP-MTP-02Brand: Metallography World Corporation
 META-Thin Pour Case of 10 380ml kits Thin Pour Physical Properties   Quick Casting – Zero Shrinkage META-THIN Pour Physical Properties & Applications Mix Time 30 - 45 Seconds Working Time 2 Minut..
Showing 1 to 3 of 3 (1 Pages)

META-Thin Pour

 

Quick Casting – Zero Shrinkage

META-THIN Pour
Physical Properties & Applications
Mix Time30 - 45 Seconds
Working Time2 Minutes
Setting Time5 - 6 Minutes
Tear Strength44 lbs/sq. Inch
Durometer30 (At 15 Minutes)
Reproduction DetailExcellent

 

Thin Pour Physical Properties – Determined at 23°C (72°F) (Tested according to ISO 4823)
Base Paste – Appearance - Homogenous blue-colored runny paste, Filling loading approximately 25% silicon dioxide.

Catalyst Paste – Appearance - Homogeneous, yellow-colored runny paste, filling loading approximately 25% silicon dioxide.
Mixed Material – Appearance - Homogenous green-colored runny paste.

Mixing Time

  • 30 seconds, larger masses may take up to 60 seconds
  • Working time (prior to gelation) 4.0 - 4.5 minutes

Setting Time

  • 8 – 9 minutes. Varies with ambient temperature. Warmer temperatures accelerate the setting time. Cooler temperatures slow the setting time.

Compression Set (Recovery from deformation) – 0.5%.
Strain in Compression (A modified Modulus of Elasticity) – 6 - 7%.

Shore A30

Dimensional Change

  • After 24 hours - 0.50% Change (negative 0.50% change) this means it shrinks 0.50%
  • After 7 days - 0.50% Change (negative 0.50% change) this means it shrinks 0.50%

Tear Strength – 200 psi
Flash Point of the Polymers Used – 130°C (266°F)
Ignition Temperature of the Polymers Used – 70°C (878°F)


Fully set material may be autoclaved, but its dimensional stability may be compromised. If allowed to return to room temperature, it should return to the original shape.

Disinfection
Since the material is hydrophobic, immersion in disinfectants is acceptable. The surface color may change due to the disinfectants used.

Applications
You can take impressions of:

  • All Metals
  • Non Metals
  • Paper or Cardboard Items
  • Ceramic and Glass items

Other Uses Include:

  • Fixturing where the semi-rigid structure is desired.
  • Making joints where flexibility is required.
  • The replica is easy to remove - even if there are undercuts or grooves.
  • Cross-sectioning of the replica is easily accomplished with a knife or razor.
  • It can then be checked on an optical comparator or microscope.
  • Surface finish replication is exact with excellent optical properties.
  • Replicas are permanent - will not leach or ooze out nor outgas.
  • Wood, Marble, etc.
  • All Plastics
  • Rubber